ω-十一烯酸改性纳米碳酸钙工艺研究

采用正交实验,以ω-十一烯酸作为表面改性剂,无水乙醇为分散介质,在一定的温度下对纳米碳酸钙粉体进行表面改性研究,确定改性纳米碳酸钙的最佳工艺条件为:改性剂用量3.0%,改性温度60℃,改性时间30min。改性后的纳米碳酸钙的吸油量(液体石蜡)降为40mL/100g,活化率提高到99.52%,表明改性后的纳米碳酸钙粒子亲油性得到显著提高。沉降速率和透射电镜(TEM)测试结果表明:改性后的纳米碳酸钙在亲油性溶剂中的分散性得到显著改善,粒度分布更加均匀。     

Experimental design approach to calcium carbonate precipitation in a semicontinuous process

The production of precipitated calcium carbonate, PCC, by a semicontinuous process of slaked lime carbonation was performed in a bench-scale chemical reactor, fully controlled by means of custom built electronics and software for the personal computer. Calcite crystals, with different characteristic morphologies (rhombohedral, truncated prismatic, scalenohedral, spheroidal or chain-like agglomerates) were produced by varying a range of process parameters, like temperature, supersaturation, gas mixture flow rate, stirring rate and mass concentration of Ca(OH)₂ suspension. In order to identify the effects of the chosen process parameters on the PCC morphology and on the related specific surface area, as well as on the extent of CO₂ conversion, an empirical approach based on the experimental design techniques was employed. A multiple correlation analysis of the obtained data suggests that temperature and conductivity significantly influence the PCC morphology, while CO₂ conversion is principally influenced by stirring rate, conductivity and gas mixture flow rate.     

钙质微波炉用耐热陶瓷釉的研究

以CaO -Al2 O3-SiO2 三元系统组成为基础研制了一种适合耐热微波炉用的平滑光亮陶瓷釉 ,该釉的坯釉结合性、热稳定性及釉面质量均符合微波炉用耐热陶瓷的要求 ,釉α80 0℃ =6 .0 1× 10 - 6 ℃ - 1 ;热稳定性可达 36 0℃～ 2 0℃热交换一次不裂 ;该种钙质耐热釉加入过多碳酸锂 ,会使坯釉结合性变差。     

海藻酸钙微胶囊的制备

研究了海藻酸钙微胶囊的制备条件和影响因素。试验结果表明 :海藻酸钠浓度不宜超过 3.0 % ,Ca Cl2的浓度为 1.0 %～ 4 .0 % ,适宜转速为 30 0 r· min- 1 ,下滴速率可控制在 6 0～ 90滴· m in- 1 ,成型的微胶囊浸泡在蒸馏水中存放 30 d后变化不大     

三聚氰胺氰尿酸盐阻燃聚氨酯硬泡

将三聚氰胺氰尿酸盐(MCA)作为阻燃剂,采用一步全水发泡法,制备一系列硬质聚氨酯泡沫/三聚氰胺氰尿酸盐复合材料(RPUF/MCA),采用扫描电子显微镜(SEM)、热重分析(TG)、极限氧指数(LOI)、UL-94垂直燃烧、烟密度测试、傅立叶红外光谱(FT-IR)及拉曼光谱表征,研究了MCA对硬质聚氨酯泡沫(RPUF)泡孔结构、热稳定性、阻燃性及燃烧烟气密度的影响。研究表明,MCA能够显著提高RPUF/MCA的阻燃性能,30份的MCA使RPUF/MCA30达到UL-94 V-1级别,极限氧指数达到22.0%。热重测试结果表明,MCA的添加使成炭率降低;同时发现,MCA的添加降低了RPUF/MCA泡沫复合材料的初始热分解温度和复合材料的燃烧烟气密度,有效地提高了复合材料火灾安全性能。     

Estimation of Concentration of Particles in Polymerizing Fluid during Centrifugal Casting of Functionally Graded Polymer Composites

The concentration of uniformly distributed particles in a fluid changes with time in the direction of gravitational or centrifugal force to form a concentration gradient. The change in the concentration is an outcome of velocity variation of particles in a fluid. A modified equation for terminal velocity, v _m of particles in polymerizing-fluid under centrifugal force is proposed to estimate the changes in the volume fraction of particles in the graded composites. The proposed equation introduces the effect of cure kinetics of polymer and its effect on particle movement in the model that was based on the modified Stoke’s law, considering the parameters related to particle hindrance, centrifugal force, particle dimensions, viscosity variation etc. The model predictions of concentration changes at the different locations of samples were compared with calcium carbonate filled polysulphide-modified-epoxy graded composites prepared by centrifugal casting.. The effect of particle size, delayed curing rate of matrix were explored. The simulated results are in good agreement with those of experiments.     

水热法解聚钠硼解石制备硼酸钙

以钠硼解石天然矿粉为原料，经水热解聚和相转化制备出硼酸钙产品。通过化学分析、XRD及TG—DTG分析表明：产品中的物相主要是白硼钙石（4CaO·5B2O3-7H2O）、硬硼钙石（2CaO·3B2O3·5H2O）和羟硼钙石（3CaO·2B2O3·9H2O）。实验确定了适宜的工艺条件，即：反应体系液固体积质量比为2．5mL／g左右；解聚温度120℃；解聚时间8h左右；干燥温度在200℃左右。在此工艺条件下制得的硼酸钙产品的氧化钠质量分数在0．5％以下，很好地满足了无碱玻璃纤维工业对含硼原料的要求。     

纳米级石灰石钙基脱硫试验研究

考虑到纳米微粒的粒径小,比表面大的特点,在一维热态试验台上,研究了纳米级钙基吸着剂脱硫过程.结果表明,纳米级石灰石普遍具有很好的脱硫效果,不同纳米石灰石,由于其比表面积、粒径以及内部成份、结构等的不同,脱硫率明显不同;粒径,温度和SO2浓度是影响脱硫的关键因素,在最佳温度1000℃、粒径为100nm,Ca/S=1.5和SO2浓度为2000ppm的条件下,其脱硫率可达90%以上.     

电石法氯乙烯生产过程中的环保问题及对策

阐述了电石法氯乙烯在生产过程中有可能产生的废水、废气、废渣及相应的对策,并对各种方案进行了简要的理论分析和比较。介绍了南通江山农药化工股份有限公司在电石法氯乙烯生产中解决环保问题的一些做法及取得的经济效益和社会效益。     

高温下 CaS氧化反应特性的实验研究

采用热重等温实验研究了970～1150℃内CaS的氧化反应特性,利用红外光谱仪定量分析反应析出SO2气体,通过亚甲基蓝分光光度法测定固体残留物中CaS的含量.实验研究发现,在970～1150℃内,反应呈先失重后增重趋势,固体残留物中都检测出少量CaS的存在.随温度升高,残留固体样品中CaSO4的质量百分比下降,而CaO的质量百分比上升,SO2析出速率急剧增大,1150℃下SO2的析出速率比970℃下的析出速率高了一个数量级.随O2浓度增大,残留固体样品中CaSO4的质量百分比和SO2析出速率轻微上升.降低反应温度和增大O2浓度,有利于提高CaS氧化生成CaSO4的比例.